Formfutura Engineering SLA Series - Heavy Duty Resin 500ml

Référence formfutura_engresin Marque Formfutura

Formfutura Heavy Duty Resin est un type d'ingénierie de résine photopolymère spécialement développée pour fonctionner avec toutes les imprimantes 3D SLA, DLP et LCD open source dans la plage de 385 à 405 nm. Notre résine Heavy Duty Engineering combine une résistance à la flexion impressionnante avec une résistance à haute température et une durabilité.

94,99 €
94,99 € TVAC 78,50 € HTVA
TTC

Formfutura Engineering SLA Series - Heavy Duty Resin 500ml

Key features

  • Flexural strength of 135 MPa

  • Stiff and durable

  • High heat resistance of 128°C

  • High dimensional accuracy and low shrinkage

  • Almost odorless processing

  • Compatible with all open-source SLA, DLP, and LCD 3D printers in the range of 385 - 405nm 

Applications

  • Tooling

  • Jigs and fixtures

  • Manufacturing aids

  • Mold masters for low volume injection molding

  • Functional prototyping

Resin properties (uncured liquid)

  • Viscosity: 550 cps at 25°C

  • Density: 1.12 g/cm2

Mechanical properties

Test method on post cured objects through 10 minutes high power mercury curing.

Properties

Typical Value

Test Method

Glass transition temperature (Tg)

128°C

ASTM D7028

Water absorption

0.45%

ASTM D570-98

Impact strength (IZOD notched)

20 J/m

ASTM D256A

Tensile strength

91 MPa

ASTM D638M

Tensile Modulus

2500 MPa

ASTM D638M

Elongation at break

8%

ASTM D638M

Flexural Strength

135 MPa

ASTM D790M

Flexural Modulus

3250 MPa

ASTM D2240

Shore D Hardness

87

ASTM D2240

Please note that the above-displayed values can vary with individual machine processing, post-curing parts,  geometry, print orientation, print settings, and temperature.

Preparation(s) before starting to print

  • Shake the bottle for at least 2 minutes before each use

  • After shaking the bottle, leave the resin to rest for 10 minutes to let air bubbles get out of the resin

    • The resin can be poured back from the vat into the bottle once your print is finished

  • Always use protective measurements like safety glasses and nitrile gloves when handling resins

Post-processing

We do advise you to post-process your 3D print in order to achieve the material properties.

  • Rinse your 3D printed object in IPA or (Bio)Ethanol for approximately 5 minutes

    • An ultrasonic cleaner is preferred/recommended

  • Make sure that IPA and/or (Bio)Ethanol rinsed objects are perfectly dry before further post-curing.

  • Place the rinsed parts in a well-ventilated area for at least 30 minutes, or use pressurized air for at least 2 minutes

  • Cure your object in a high power curing chamber for approximately 20-30 minutes at 65° C

  • The preferred curing wavelength is between 300-410nm

Safety

Please always be aware that when 3D printing with resins that you are working with chemicals and that you should always be cautious and use the personal protective equipment as stipulated in our safety data sheets.

  • Always wear Respiratory Protection when sanding/cutting the resin object

  • Always use nitrile gloves when handling resins and uncured resin objects

Product export information

HS Code: 2916140090 Description: Resin for 3D Printing Country of origin: the Netherlands

Caractéristiques techniques