Ultrafuse PA6 GF30

Ultrafuse PA6 GF30 contains 30% of special glass fibers that aredesigned for filament making and 3D printing. PA6 GF30 has a reduced warping compared to neat PA6 which makes Ultrafuse PA6 GF30 with its excellent layer adhesion and its compatibility with the watersoluble Ultrafuse BVOH the right solution for industrial parts printable on any standard FFF printer. With its high wear and chemical resistanceand the high stiffness and strength, Ultrafuse PA6 GF30 is perfect forvarious applications in transportation or industrial tooling for example.

Tips & Tricks

• Nozzle Temperature; 240-280 °C
• Bed Temperature; passively heated, closed chamber
• Bed modification; glass
• Drying Procedure; Dry the filament at 100°C for at least 5 hours
• Support Materials; BVOH
• Nozzle Diamater; ? 0.6 mm
• Print Speed; 30-60 mm/sec

Material Properties

• Tensile Strength (MPa): 78,3 / 46,4 (XY), 14,9 / 12,2 (ZX)
• Flexural Modulus (MPa): 4694 / 2861 (XY), 8103 / 4300 (XZ), 2371 / 1070 (ZX)
• Elongation at Break: 2.2 / 3.2 % (XY), 0,8 / 1,9 % (ZX)
• Impact Strength Charpy unnotched (kJ/m2): 38,9 / 41,8 (XY) , 45,5 / 48,8 (XZ) , 2,2 / 3,1 (ZX)
• Impact Strength Izod unnotched (kJ/m2): 38,4 / 36,9 (XY) , 38,7 / 41,4 (XZ) , 2,6 / 3,8 (ZX)
• HDT @ 0,45 MPa: 110 / 114 oC

BASF Quality Control